A Comparison of the Effect of three Direct Composite Restoration Techniques on the Fracture Resistance of Endodontically Treated Maxillary Premolars
H Kazemi yazdi Dr *, N Aryan Dr, M SHahbazi moghadam Dr
, haleh1352@yahoo.com
Abstract:   (7813 Views)


Background and aim: Failure of restored teeth after endodontic treatment is one of the challenges faced in restorative dentistry. Premolar teeth are more likely to fracture due to exposure to tensile stress and inappropriate anatomical shape. Therefore, the aim of this study was the comparison of the fracture resistance of maxillary premolars which were restored with composite resin, composite resin with glass ionomer lining and composite resin reinforced with fiber post.




Materials and Methods: In this experimental study, 60 extracted human maxillary premolars were randomly divided into 4 groups of 15: Composite resin without bonding (1), Composite resin+ glass ionomer lining (2), Composite resin+ single bond 2 (3) and Composite resin+ Fiber post (4). The teeth were prepared by MOD design with palatal cusp reduction. The samples were placed in a chewing simulator and went under a 30 N force for 1200000 cycles. The threshold of compressive resistance was measured in MPa. Also, fracture patterns were assessed divided by restorability and non-restorability. ANOVA test was used for statistical analysis of data in all groups and post-hoc TUKEY test was used for two by two comparisons.




Results: The threshold of force resistance significantly increased from group 1 to 4 and the difference among all groups was strongly significant (p = 0.000). Restorable fracture pattern followed an ascending order from group 1 to 4 which was reversed for unrestorable pattern with no significance. (P> 0.05)




Conclusions: Composite resin restoration reinforced with fiber post can increase the fracture resistance of endodontically treated premolars but the number of unrestorable fractures also increases with the use of these posts. Fracture strength and fracture patterns obtained through usage of composite resin restorations in endodontically treated teeth are appropriate.




Keywords: Composite Resins, Dentin-Bonding Agents, Glass Ionomer Cements, Post and Core Technique, Stress
Full-Text [PDF 12 kb]   (1144 Downloads)    
Type of Study: original article | Subject: oral surgery
Send email to the article author

Add your comments about this article
Your username or Email:


XML   Persian Abstract   Print

Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

kazemi yazdi H, Aryan N, SHahbazi moghadam M. A Comparison of the Effect of three Direct Composite Restoration Techniques on the Fracture Resistance of Endodontically Treated Maxillary Premolars. J Res Dent Sci. 2015; 11 (4) :206-214
URL: http://jrds.ir/article-1-553-en.html

Volume 11, Issue 4 (J Res Dent Sci 2015) Back to browse issues page
مجله تحقیق در علوم دندانپزشکی Res Dent Sci
Persian site map - English site map - Created in 0.07 seconds with 32 queries by YEKTAWEB 3877