J Res Dent Sci 2016, 13(3): 122-128 Back to browse issues page
The Effect of incorporation of UHMWPE fiber and Silica nanoparticles on mechanical properties of dental Composite resin
N Bahramian, M Atai, M R Naimi-Jamal
, m.atai@ippi.ac.ir
Abstract:   (7851 Views)

Background & aim: Fiber reinforced composite (FRC) has become a considerable material in restorative dentistry.  In this work the effect of different UHMWPE fiber content and fumed silica nanoparticle incorporation on the flexural properties and fracture toughness of UHMWPE fiber-reinforced dental composite was studied.

Materials and Methods: FRC used in this experimental study, was made of  BisGMA/TEGDMA (70/30) resin and silanized corona treated UHMWPE fibers. The flexural strength and flexural modulus of the FRCs were determined on 2 mm×2 mm×25 mm specimens. The fracture toughness (the critical stress intensity factor, KIC) of the composites was also evaluated using a three-point single edge notch beam (SENB) bending technique. To investigate the effect of fiber content on mechanical properties, three different fiber volume fraction (41%, 33% and 25%) were used. Treated nanosilica filler with different weight percentage (0wt%, 10 wt% and 15 wt%) were added to composite samples to evaluate the effect of nanoparticle  incorporation on mechanical properties. The nanoparticles distribution was studied by transmission electron microscopy (TEM). The results were submitted to statistical analysis through ANOVA complemented by Tukey’s test at a significance level of 5%.

Results: The results show that flexural strength, flexural modulus and fracture toughness of the samples increases with increase in the fiber percentage and this increasing in FRC is significant (P˂0.05), (flexural strength (225.7±22.2 MPa), flexural modulus (45.225±5.1 GPa), fracture toughness (6.832±1.3 MPa.m1/2). Nanoparticles incorporation (10%wt, 15%wt) show significant reduction (P˂0.05) in flexural strength of the composites.

Conclusion: Fracture toughness and flexural properties of FRC increase with increasing fiber content. Also nanoparticles distribution and dispersion are two important factors to determine mechanical properties of hybrid composites.  

Keywords: dental composites, Bis-GMA, UHMWPE, fiber, nanoparticles
Full-Text [PDF 75 kb]   (2508 Downloads)    
Type of Study: original article | Subject: Dental materiall
Send email to the article author

Add your comments about this article
Your username or Email:

CAPTCHA


XML   Persian Abstract   Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

Bahramian N, Atai M, Naimi-Jamal M R. The Effect of incorporation of UHMWPE fiber and Silica nanoparticles on mechanical properties of dental Composite resin . J Res Dent Sci 2016; 13 (3) :122-128
URL: http://jrds.ir/article-1-787-en.html


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
Volume 13, Issue 3 (Jrds 2016) Back to browse issues page
مجله تحقیق در علوم دندانپزشکی Res Dent Sci
Persian site map - English site map - Created in 0.05 seconds with 30 queries by YEKTAWEB 4540